2*C(s)+O_2(g)=2*CO(g)	T=300,2000	O	1    F
2*CO(g)+O_2(g)=2*CO_2(g)	T=300,2000	O	2     F    		
C(s)+O_2(g)=CO_2(g)	T=300,2000	O	3  F
2*Zn(s)+O_2(g)=2*ZnO(s)	T=300,693	N	4   T
2*Zn(l)+O_2(g)=2*ZnO(s)	T=693,1180	N	4  T
2*Zn(g)+O_2(g)=2*ZnO(s)	T=1180,2000	O	4 F
1.5*Fe(s)+O_2(g)=0.5*Fe_3O_4(s)		T=300,1811	N	5 T
1.5*Fe(l)+O_2(g)=0.5*Fe_3O_4(s)	T=1811,2000	O	5 F
2*H_2(g)+O_2(g)=2*H_2O(l)		T=300,373	N	6    T
2*H_2(g)+O_2(g)=2*H_2O(g)		T=373,2000	O	6   F
Si(s)+O_2(g)=SiO_2(s)		T=300,1687	N	7   T
Si(l)+O_2(g)=SiO_2(s)		T=1687,2000	O	7  F
1.33*Al(s)+O_2(g)=0.66*Al_2O_3(s)	T=300,933	N	8 T
1.33*Al(l)+O_2(g)=0.66*Al_2O_3(s)	T=933,2000	O	8    F
2*Pb(s)+O_2(g)=2*PbO(s)		T=300,600	N	9  T
2*Pb(l)+O_2(g)=2*PbO(s)		T=600,2000	O	9 F
2*Cu(s)+O_2(g)=2*CuO(s)		T=300,1360	N	10    T
2*Cu(l)+O_2(g)=2*CuO(s)		T=1360,1599	N	10   T
2*Cu(l)+O_2(g)=2*CuO(l)     T=1599,2000 O   10  F
2*Fe(s)+O_2(g)=2*FeO(s)     T=300,1633  N   11  T
2*Fe(s)+O_2(g)=2*FeO(l)     T=1633,1808  N   11 T
2*Fe(l)+O_2(g)=2*FeO(l)     T=1808,2000  O   11 F
6*FeO(s)+O_2(g)=2*Fe_3O_4(s)    T=300,1633  N   12  T
6*FeO(l)+O_2(g)=2*Fe_3O_4(s)    T=1633,1867 N   12  T
6*FeO(l)+O_2(g)=2*Fe_3O_4(l)    T=1867,2000  O   12 F
4*Fe_3O_4(s)+O_2(g)=6*Fe_2O_3(s)    T=300,1750  O   13  F
2*Mg(s)+O_2(g)=2*MgO(s)     T=300,923   N   14  T
2*Mg(l)+O_2(g)=2*MgO(s)     T=923,1383   N   14 T
2*Mg(g)+O_2(g)=2*MgO(s)     T=1383,2000   O   14    F
4*Ag(s)+O_2(g)=2*Ag_2O(s)   T=300,1235  N   15  T
4*Ag(l)+O_2(g)=2*Ag_2O(s)   T=1235,2000  O   15 F
2*Mn(s)+O_2(g)=2*MnO(s)     T=300,1517  N   16  T
2*Mn(l)+O_2(g)=2*MnO(s)     T=1517,2000 O 16    F
1.33*Cr(s)+O_2(g)=0.66*Cr_2O_3(s)   T=300,2000  O   17  F